Bi2WO6 powders were synthesized by the molten salt method at 250-350 ºC using the mixture of Bi(NO3)3·5H2O and Na2WO4·2H2O as a precursor, and the mixture of LiNO3 and NaNO3 with a molar ratio of 27:33 as a molten salt, respectively. The effects of temperature and salt amount on the phase composition, morphology and photocatalytic activity under the visible light irradiation were investigated. The results revealed that pure phase Bi2WO6 powders could be synthesized at 350 ºC as the weight of molten salts were 2‒5 times as many as the precursor. Bi2WO6 powder synthesized with lower salt amount exhibited larger surface area, more abundant pores, narrower bandgap and lower PL intensity, all of which contributed a higher photocatalytic activity. The synthesized Bi2WO6 powder could degrade 0.01 mol/L Rhodamine-B solution by 97% after irradiation under visible light for 60 min. The obtained Bi2WO6 powder had a good photochemical stability and reusability, revealing potential application in environmental treatment.

Flower - like Co(OH)2/C nanocomposites have been synthesized by a facile hydrothermal method. Flower - like Co(OH)2/C nanocomposites were self - assembled by the nanosheets with the thickness distribution of 50 - 80 nm and abundant flocculent carbon structures. With the help of transmission electron microscopy and energy dispersive spectrometer, nanosheets were observed to have core/shell structure, in which Co(OH)2 worked as cores and amorphous C as shells. When the as - prepared products were heated for 6 h at 180 ºC, the Co(OH)2 cores were amorphous. The heating time increased to 10 h, the Co(OH)2 cores became crystalline. The formation mechanism and the self - assembly evolution process were proposed. The microwave dielectric properties of Co(OH)2/C nanocomposites were investigated in the frequency range of 0.03 - 18 GHz. Compared with the amorphous Co(OH)2/C nanocomposites, crystalline nanocomposites had the better conductivity.

The microstructure and microwave absorption of carbon-coated Cu nanocapsules have been investigated. Carbon-coated Cu nanocapsules have been synthesized by an arc-discharge method. The paraffin-Cu/C nanocapsules composite shows excellent electromagnetic (EM) absorption properties. An optimal reflection loss (RL) value of - 40.0 dB is reached at 10.52 GHz for a layer 1.9 mm thickness. RL exceeding - 20 dB can be realized in any interval within the 1-18 GHz range by choosing an appropriate thickness of the absorbent layer between 1.1 and 10.0 mm. Theoretical simulation for the microwave absorption using the transmission line theory agrees reasonably well with the experimental results. The EM-wave absorption properties of nanocapsules materials are illustrated by means of an absorption-tube-map. The carbon-coated Cu nanocapsule is an attractive candidate for EM-wave absorption, which significantly enriches the family of EM-wave nanoabsorbents.

A facile hydrothermal strategy is proposed to synthesize flower-like β-Co(OH)2 hierarchical microspherical superstructures with a diameter of 0.5-1.5 μm, which are self-assembled by β-Co(OH)2 nanosheets with the average thickness ranging between 20 and 40 nm. The magnetocaloric effect associated with magnetic phase transitions in Co(OH)2 superstructures has been investigated. A sign change in the magnetocaloric effect is induced by a magnetic field, which is related to a filed-induced transition from the antiferromagnetic to the ferromagnetic state below the Néel temperature. The large reversible magnetic-entropy change -ΔSm (13.4 J/kg K at 15 K for a field change of 5 T) indicates that flower-like Co(OH)2 superstructures is a potential candidate for application in magnetic refrigeration in the low-temperature range.